سال انتشار: ۱۳۸۸

محل انتشار: ششمین کنگره بین المللی مهندسی شیمی

تعداد صفحات: ۴

نویسنده(ها):

P Esmaeilnejad-Ahranjani – Catalysis and Nanostructured Materials Research Laboratory, School of Chemical Engineering, University of Tehran, Tehran, Ir an
Y Mortazavi – Catalysis and Nanostructured Materials Research Laboratory, School of Chemical Engineering, University of Tehran, Tehran, Ir an
A Khodadadi – Catalysis and Nanostructured Materials Research Laboratory, School of Chemical Engineering, University of Tehran, Tehran, Ir an
H Ziaei-Azad – Catalysis and Nanostructured Materials Research Laboratory, School of Chemical Engineering, University of Tehran, Tehran, Ir an

چکیده:

Mixed oxides of manganese-copper and manganese-copper-lanthanum with the mole ratio of Cu/ Mn=0.2 and Mn/La=1 have been prepared and evaluated in CO combustion. The gel combustion method used for the synthesis of MnCu0.2Ox and LaMnCu0.2O3+d mixed oxides is adequate to obtain catalysts with excellent catalytic performance in combustion reactions. Catalysts were characterized by means of BET, XRD, H2-TPR. The catalytic activity of the perovskite samples (for low-temperature oxidation) was measured using a quartz reactor with an inlet gas containingCO as pollutant gas, O2 and Ar as an inert gas. The mixed oxide catalysts showed high activity for the catalytic CO oxidation reaction. LaMnCu0.2O3 achieved the same CO conversion at lower temperatures than to Cu0.2MnOx.